LOW CEMENT CASTABLES - PRODUCT DATA
Properties | CERA-CAST LC-45 | CERA-CAST LC-60 | CERA-CAST LC-70 | CERA-CAST LC-80 | CERA-CAST LC-90 | CERA-CAST LC-95 |
Max.service tem.°C | 1550 | 1600 | 1650 | 1700 | 1750 | 1800 |
Setting | Hydraulic | Hydraulic | Hydraulic | Hydraulic | Hydraulic | Hydraulic |
Max grain size(mm) | 6 | 6 | 6 | 6 | 6 | 6 |
% of water required for casting | 4.5-5.5 | 4.5-5.5 | 4.5-5.5 | 4.5-5.5 | 4.5-5.0 | 4.5-5.0 |
BD gm/cc min(on vibrated block) dried at 110°C | 2.30 | 2.60 | 2.65 | 2.85 | 2.95 | 3.05 |
CCs (kg/cm2)min | ||||||
After drying at 110°C | 700 | 700 | 700 | 750 | 800 | 850 |
After firing to 800°C/2 hrs | 800 | 800 | 800 | 800 | 900 | 1000 |
After firing to 1100°C/2 hrs | 800 | 800 | 800 | 800 | 900 | 1000 |
After firing to 1550°C/2 hrs | 1000 | 1000 | 1000 | 1100 | 1150 | 1200 |
PLC % max | ||||||
At 800°C/2 hrs | +-0.2 | +-0.2 | +-0.2 | +-0.2 | +-0.2 | +-0.2 |
At 1200°C/2 hrs | +-0.3 | +-0.3 | +-0.3 | +-0.3 | +-0.3 | +-0.3 |
At 1500°C/2 hrs | +-0.1 | +-0.1 | +-0.8 | +-0.6 | +-0.6 | +-0.6 |
Chemical Analyis | ||||||
AL2O3 % min. | 45 | 60 | 70 | 80 | 90 | 95 |
Fe2O3 % max. | 1.0 | 1.5 | 1.5 | 1.8 | 1.0 | 0.3 |
CaO % max | 2.5 | 2.5 | 2.0 | 2.0 | 2.0 | 2.0 |